Surface modification for titanium implants by hydroxyapatite nanocomposite
چکیده:   (22212 مشاهده)
Background: Titanium (Ti) implants are commonly coated with hydroxyapatite (HA). However, HA has some disadvantages such as brittleness, low tensile strength and fracture toughness. It is desirable to combine the excellent mechanical properties of ZrO2 and the chemical inertness of Al2O3 with respect to the purpose of this project which was coating Ti implants with HA-ZrO2-Al2O3 to modify the surface of these implants by adding ZrO2 and Al2O3 to HA. The purpose of this study was to evaluate the efficacy of hydroxyapatite coating nonocomposite.
Methods: From September 2009 to January2011, functionally graded HA-Al2O3-ZrO2 and HA coatings were applied on Ti samples. HA-Al2O3-ZrO2 and HA sols were orderly dip coated on the substrates and calcined. Scanning electron microscopy and EDS were used to estimate the particle size of the surfaces and for morphological analysis. The morphology of non-coated HA-coated HA-Al2O3-ZrO3 (composite-coated) and double-layer composite coated samples were compared with one other. Mechanical test (heat & quench) was also done for comparing single-phase (HA), composite and double-layer composite samples.
Results: The morphology of HA-Al2O3-ZrO2 coating is more homogenous than HA-coated and uncoated samples. Furthermore, single-layer coating is more homogenous than double-layer coating. EDS analysis was done on HA-coated sample and showed that the Ca/P ratio in the film was similar to the theoretical value 1.67 in HA.
Conclusion: Surface modification of Ti implants can be done by coating them with single-layer of HA-Al2O3-ZrO2. Single-layer hydroxyapatite-alumina-zirconia coated sample has the most homogenous morphology on the surface.
متن کامل [PDF 1224 kb]   (2191 دریافت)    
نوع مطالعه: Original Article | موضوع مقاله: Infectious Diseases
دریافت: ۱۳۹۲/۱۰/۲۵ | پذیرش: ۱۳۹۲/۱۰/۲۵ | انتشار: ۱۳۹۲/۱۰/۲۵
ارسال نظر درباره این مقاله
نام کاربری یا پست الکترونیک شما:

CAPTCHA code


XML   English Abstract   Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Family R, Solati-Hashjin M, Namjoy Nik S, Nemati A. Surface modification for titanium implants by hydroxyapatite nanocomposite. Caspian J Intern Med. 2012; 3 (3) :460-465
URL: http://caspjim.com/article-1-157-fa.html

Surface modification for titanium implants by hydroxyapatite nanocomposite. 1. 1390; 3 (3) :460-465

URL: http://caspjim.com/article-1-157-fa.html



دوره 3، شماره 3 - ( 10-1390 ) برگشت به فهرست نسخه ها
Caspian Journal of Internal Medicine
Persian site map - English site map - Created in 0.05 seconds with 31 queries by YEKTAWEB 3792